Gauntlet For
Lead Acid Batteries
|
QUALITY
|
MATERIAL CODE
|
SPECIFICATION
|
|
12mm
x 115mm x 11 tubes
|
PT1201
|
|
|
9mm
x 9mm x 110.5 mm x 6 tubes
|
PT9001
|
|
|
10mm
x 109 mm x 5 tubes
|
PT1001
|
|
|
7.24mm
x 175mm x 15 tubes
|
PT7201
|
|
|
8mm
x 240mm x 15 tubes
|
PT8008
|
|
|
8.4mm
x 160mm x 15 tubes
|
PT8404
|
|
|
8mm
Square x 255mm x 15 tubes
|
PS8401
|
|
|
6.2mm
x 256.5mm x 22 tubes
|
PTB012
|
|
12mm
x 115mm x 11 Tubes
| MATERIAL
|
100%
POLYESTER YARN
|
| MAJOR
AXIS (mm) |
12.0
± 0.2
|
| MINOR
AXIS (mm) |
5.70
± 0.2
|
| INNER
RADIUS (mm) |
2.85
|
| PITCH
(mm) |
13.2
± 0.1
|
| PITCH
BETWEEN END TUBES (mm) |
132
± 0.25
|
| NO.
OF TUBES |
11
|
| LENGTH
(mm) |
115
± 0.3
|
| RESIN
(mm) |
ACRYLIC
|
| RESIN
CONTENT (%) |
22
± 2
|
| BREAKING
LOAD (kgf/cm) |
|
|
WARP
|
67
|
|
WEFT
|
65
|
| WEIGHT
LOSS AFTER REFLUX IN |
|
| 1.2S.G.
H2SO4 FOR 2 HOURS (%) |
0.2
|
[TOP]
9mm
x 9mm x 110.5 mm x 6 Tubes
| MATERIAL
|
100%
POLYESTER YARN
|
| INNER
DIAMETER (mm) |
9
X 9 + 0.1 - 0
|
| INNER
RADIUS (mm) |
0.4
|
| PITCH
(mm) |
10.35
± 0.1
|
| PITCH
BETWEEN END tubes (mm) |
51.75
± 0.25
|
| NO.
OF TUBES |
6
|
| LENGTH
(mm) |
110
± 0.3
|
| RESIN
(mm) |
ACRYLIC
|
| RESIN
CONTENT (%) |
22
± 2
|
| BREAKING
LOAD (kgf/cm) |
|
|
WARP
|
67
|
|
WEFT
|
65
|
| WEIGHT
LOSS AFTER REFLUX IN |
|
| 1.2S.G.
H2SO4 FOR 2 HOURS (%) |
0.2
|
[TOP]
10mm
x 109 mm x 5 Tubes
| MATERIAL
|
100%
POLYESTER YARN
|
| INNER
DIAMETER(mm) |
10.0
± 0.08
|
| PITCH
(mm) |
11.3
± 0.1
|
| PITCH
BETWEEN END tubes (mm) |
45.2
± 0.2
|
| LENGTH
(mm) |
109
± 0.3
|
| NO
OF TUBES |
5 |
| RESIN
(mm) |
ACRYLIC
|
| RESIN
CONTENT (%) |
24
± 2
|
| BREAKING
LOAD (kgf/cm) |
|
|
WARP
|
67
|
|
WEFT
|
65
|
| WEIGHT
LOSS AFTER REFLUX IN |
|
| 1.2S.G.
H2SO4 FOR 2 HOURS (%) |
0.2
|
| MATERIAL
|
100%
POLYESTER YARN
|
| INNER
DIAMETER (mm) |
7.24
± 0.1
|
| PITCH
(mm) |
9.60
± 0.1 & 8.9 ± 0.1
|
| PITCH
BETWEEN END tubes (mm) |
134.4±
0.5
|
| LENGTH
(mm) |
95
- 560 ± 0.3
|
| RESIN
(mm) |
ACRYLIC
|
| RESIN
CONTENT (%) |
22
± 2
|
| BREAKING
LOAD (kgf/cm) |
|
|
WARP
|
70
|
|
WEFT
|
65
|
| WEIGHT
LOSS AFTER REFLUX IN |
|
| 1.2S.G.
H2SO4 FOR 2 HOURS (%) |
0.2
|
[TOP]
8mm
x 240mm x 15 TUBES
| MATERIAL
|
100%
POLYESTER YARN
|
| INNER
DIAMETER (mm) |
8.00
± 0.1
|
| PITCH
(mm) |
9.20
& 9.70 ± 0.1
|
| PITCH
BETWEEN END tubes (mm) |
135.8
± 0.5
|
| LENGTH
(mm) |
95
- 560
|
| RESIN
(mm) |
ACRYLIC
|
| RESIN
CONTENT (%) |
22
± 2
|
| BREAKING
LOAD (kgf / cm) |
|
|
WARP
|
70
|
|
WEFT
|
65
|
| WEIGHT
LOSS AFTER REFLUX IN |
|
| 1.2S.G.
H2SO4 FOR 2 HOURS (%) |
0.2
|
[TOP]
8.4mm
x 160mm x 15 TUBES
| MATERIAL
|
100%
POLYESTER YARN
|
| INNER
DIAMETER (mm) |
8.40
± 0.1
|
| PITCH
(mm) |
9.70
± 0.1
|
| PITCH
BETWEEN END tubes (mm) |
135.5±
0.5
|
| LENGTH
(mm) |
95
- 560
|
| RESIN
|
ACRYLIC
|
| RESIN
CONTENT (%) |
22
± 2
|
| BREAKING
LOAD (kgf/cm) |
|
|
WARP
|
67
|
|
WEFT
|
65
|
| WEIGHT
LOSS AFTER REFLUX IN |
|
| 1.2S.G.
H2SO4 FOR 2 HOURS (%) |
0.2
|
[TOP]
8mm
SQUARE x 255mm x 15 TUBES
| MATERIAL
|
100%
POLYESTER YARN
|
| MAJOR
AXIS (mm) |
8.40
± 0.2 |
| MINOR
AXIS (mm) |
9.60
± 0.2 |
| PITCH
(mm) |
9.53
± 0.1
|
| PITCH
BETWEEN END tubes (mm) |
133
± 0.5
|
| LENGTH
(mm) |
255
± 0.3
|
| RESIN
(mm) |
ACRYLIC
|
| RESIN
CONTENT (%) |
22
± 2
|
| BREAKING
LOAD (kgf/cm) |
|
|
WARP
|
67
|
|
WEFT
|
65
|
| WEIGHT
LOSS AFTER REFLUX IN |
|
| 1.2S.G.
H2SO4 FOR 2 HOURS (%) |
0.2
|
[TOP]
6.2mm
x 256.5mm x 22 Tubes
| MATERIAL |
100%
POLYESTER YARN |
|
INNER DIAMETER (mm) |
6.22
± 0.08
|
| PITCH
|
7.6
mm ± 0.1
|
| PITCH
BETWEEN END tubes |
|
| LENGTH
(mm) |
256.5
|
| RESIN
|
Acrylic
|
| RESIN
CONTENT (%) |
22 ± 2
|
| BREAKING
LOAD |
|
|
WARP
|
67
|
|
WEFT
|
65
|
| WEIGHT
LOSS AFTER REFLUX IN |
|
| 1.2S.G.
H2SO4 FOR 2 HOURS (%) |
0.36
|
[TOP]
|